Using high raw materials, calcined alumina is being produced in the rotary kiln on the reasonable temperature, with the characteristic of high conversion rate, stable crystallization and low impurity content.
Its products have excellent performance of high mechanical strength, stable shrinkage rate, good electrical insulation, high wear resistance, and outstanding corrosion resistance.
Brand | chemical components % |
α-Al2O3%≥ | effective density g/cm3 ≥ |
Primary crystal size D50 μm | ||||
Al2O3≥ |
SiO2≤ |
Fe2O3≤ |
Na2O≤ |
L.O.L≤ | ||||
A-C-30 | 99.0 | 0.10 | 0.04 | 0.35 | 0.20 | 94 | 3.93 | 4±1 |
A-C-3-A | 99.0 | 0.10 | 0.04 | 0.35 | 0.20 | 93 | 3.93 | 2.5±1 |
A-C-40 | 99.4 | 0.20 | 0.07 | 0.40 | 0.25 | 90 | 3.90 | - |
Using high raw materials, calcined alumina is being produced in the rotary kiln on the reasonable temperature, with the characteristic of high conversion rate, stable crystallization and low impurity content.
Its products have excellent performance of high mechanical strength, stable shrinkage rate, good electrical insulation, high wear resistance, and outstanding corrosion resistance.
Application:
l various abrasives, abrasive tools and fillers
l fine powder of various ceramic and refractory grade alumina
l high alumina structural ceramic
l electronic components, high insulating ceramic
Brand | chemical components % | Particle size | |||||
Al2O3≥ |
SiO2≤ |
Fe2O3≤ |
Na2O≤ |
L.O.L≤ | median particle sizeD50 μm |
screen residue ≤ | |
A-CG-2-A | 99.0 | 0.2 | 0.04 | 0.35 | 0.25 | 1-3 | - |
A-CG-1-A | 99.2 | 0.2 | 0.04 | 0.3 | 0.25 | ≤1 | - |
A-C-10-LS | 99.5 | 0.1 | 0.04 | 0.1 | 0.2 | ≤1 | - |
Excellent sintering performance, stable linear shrinkage,suitable particle size and narrow particle size distribution. Widely used in refractory and ceramic industries.
Application:
l Refractories, refractory binder
l High-alumina ceramic.High-alumina glaze
l Glass
l Polishing materials
Brand | AC-200MS | AC-200LS | AC-200LLS | AC-300MS | AC-300LS | AC-300LLS |
Al2O3≥ | 99.0 | 99.5 | 99.5 | 99.0 | 99.5 | 99.5 |
SiO2≤ | 0.02 | 0.02 | 0.02 | 0.02 | 0.02 | 0.02 |
Fe2O3≤ | 0.02 | 0.02 | 0.02 | 0.02 | 0.02 | 0.02 |
Na2O≤ | 0.20 | 0.10 | 0.05 | 0.20 | 0.10 | 0.05 |
L.O.L≤ | 0.20 | 0.10 | 0.10 | 0.20 | 0.10 | 0.10 |
α-Al2O3%≥ | 93 | 94 | 95 | 93 | 94 | 95 |
crystallinity μm |
2±1 |
2±1 |
2±1 |
3±1 |
3±1 |
3±1 |
effective density g/cm3≥ |
3.93 |
3.94 |
3.95 |
3.93 |
3.94 |
3.95 |
Calcined alumina is made of high-quality raw materials and calcined at high temperature. It has the advantages of high conversion rate, stable crystal shape and low impurity content. Its products have high mechanical strength, stable shrinkage rate, good electrical insulation performance, excellent wear resistance, corrosion resistance and high temperature resistance.
Features
High α-Al2O3% content
No mineralization, low sodium oxide content, high purity
Excellent particle distribution
Application
High quality refractory material
Electronics and Advanced Ceramics
Wear-resistant alumina ceramics
Brand | ACG-200 MS | ACG-200L S | ACG-200LL S | ACG-300 MS | ACG-300L S | ACG-300LL S |
Al2O3≥ | 99 | 99.5 | 99.5 | 99 | 99.5 | 99.5 |
SiO2≤ | 0.02 | 0.02 | 0.02 | 0.02 | 0.02 | 0.02 |
Fe2O3≤ | 0.04 | 0.04 | 0.04 | 0.04 | 0.04 | 0.04 |
Na2O≤ | 0.2 | 0.1 | 0.05 | 0.2 | 0.1 | 0.05 |
L.O.L≤ | 0.3 | 0.2 | 0.1 | 0.3 | 0.2 | 0.1 |
α-Al2O3% ≥ | 93 | 94 | 95 | 93 | 94 | 95 |
Particle size μm | 2±1 | 2±1 | 2±1 | 4±1 | 4±1 | 4±1 |
Calcined α alumina micro powder takes calcined α alumina raw powder as raw material, and is processed and ground into micro powder products with reasonable particle size distribution and high thermal stability. For wear-resistant ceramics, anti-insulators, thermally conductive resins, transparent ceramics, etc.
Features
Reasonable particle size distribution
good uniformity
High thermal stability
APPLICATIONS:
High quality refractory material
Electronics and Advanced Ceramics
Wear-resistant alumina ceramics